Polycarbonate-polyorganosiloxane copolymer, polycarbonate resin composition including same, and molded product thereof

ABSTRACT

Provided is a polycarbonate-polyorganosiloxane copolymer including polycarbonate blocks (A-1) each formed of a specific repeating unit and polyorganosiloxane blocks (A-2) each containing a specific repeating unit, wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F1a): 
       15≤ wM 1  (F1a)
 
     wherein wM1 represents the average content of the polyorganosiloxane blocks (A-2) in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using a polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by gel permeation chromatography.

TECHNICAL FIELD

The present invention relates to a polycarbonate-polyorganosiloxane copolymer, a polycarbonate-based resin composition including the copolymer, and a molded article of the composition.

BACKGROUND ART

A polycarbonate-polyorganosiloxane copolymer (hereinafter sometimes abbreviated as “PC-POS copolymer”) has been attracting attention because of its excellent properties, such as high impact resistance, chemical resistance, and flame retardancy. Accordingly, the polycarbonate-polyorganosiloxane copolymer has been expected to be widely utilized in various fields, such as the field of electrical and electronic equipment and the field of automobiles. In particular, the utilization of the polycarbonate-polyorganosiloxane copolymer in casings for a cellular phone, a mobile personal computer, a digital camera, a video camera, an electric tool, a communication base station, a battery, and the like, and in other commodities has been expanding.

In normal cases, a homopolycarbonate using 2,2-bis(4-hydroxyphenyl)propane [common name: bisphenol A] as a dihydric phenol serving as a raw material has been generally used as a typical polycarbonate. A polycarbonate-polyorganosiloxane copolymer using a polyorganosiloxane as a copolymerizable monomer has been known for improving the physical properties of the homopolycarbonate, such as flame retardancy and impact resistance (Patent Document 1).

Examples of an approach to further improving the impact resistance of a polycarbonate resin containing the polycarbonate-polyorganosiloxane copolymer may include an approach involving using a polyorganosiloxane having a long chain length, and an approach involving increasing the amount of the polyorganosiloxane in the polycarbonate-polyorganosiloxane copolymer as described in Patent Documents 2 and 3.

CITATION LIST Patent Document

Patent Document 1: JP 2662310 B2

Patent Document 2: JP 2011-21127 A

Patent Document 3: JP 2012-246390 A

SUMMARY OF INVENTION Technical Problem

As described above, the polycarbonate-polyorganosiloxane copolymer is excellent in impact resistance, but it has been required to obtain a polycarbonate-based resin composition further improved in chemical resistance.

Solution to Problem

The inventors of the present invention have found that, when a polycarbonate-polyorganosiloxane copolymer whose polyorganosiloxane block concentration in a specific molecular weight region is equal to or more than a certain value is used, a polycarbonate-polyorganosiloxane copolymer having more excellent impact resistance is obtained without the extension of the chain length of a polyorganosiloxane block or an increase in content thereof. In addition, the inventors have found that the addition of a polyester-based resin to a polycarbonate-based resin including the polycarbonate-polyorganosiloxane copolymer provides a polycarbonate-based resin composition further excellent in chemical resistance.

That is, the present invention relates to the following items [1] to [27].

[1] A polycarbonate-polyorganosiloxane copolymer, comprising:

polycarbonate blocks (A-1) each formed of a repeating unit represented by the following general formula (I); and

polyorganosiloxane blocks (A-2) each containing a repeating unit represented by the following general formula (II),

wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F1a):

15≤wM1  (F1a)

wherein wM1 represents an average content (mass %) of the polyorganosiloxane blocks (A-2) in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using a polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among polycarbonate-polyorganosiloxane copolymers obtained through separation of the polycarbonate-polyorganosiloxane copolymer by gel permeation chromatography;

wherein R¹ and R² each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, a fluorenediyl group, an arylalkylene group having 7 to 15 carbon atoms, an arylalkylidene group having 7 to 15 carbon atoms, —S—, —SO—, —SO₂—, —O—, or —CO—, R³ and R⁴ each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and “a” and “b” each independently represent an integer of from 0 to 4.

[2] The polycarbonate-polyorganosiloxane copolymer according to the above-mentioned item [1], wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F1a′):

13≤wM2  (F1a′)

wherein wM2 represents an average content (mass %) of the polyorganosiloxane blocks (A-2) in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 16,000 or more to less than 56,000 among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography.

[3] The polycarbonate-polyorganosiloxane copolymer according to the above-mentioned item [1] or [2], wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F1b):

100<wM1/wA×100  (F1b)

wherein wM1 is as described above, and wA represents an average content (mass %) of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymer.

[4] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [3], wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F2):

wM2<wM1  (F2)

wherein wM1 and wM2 are as described above.

[5] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [4], wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F3):

wM3<wM2  (F3)

wherein wM2 is as described above, and wM3 represents an average content (mass %) of the polyorganosiloxane blocks (A-2) in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 4,500 or more to less than 16,000 among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography.

[6] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [5], wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F4a):

50≤nM1  (F4a)

wherein nM1 represents an average chain length of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography.

[7] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [6], wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F4b):

100<nM1/nA×100  (F4b)

wherein nM1 is as described above, and nA represents an average chain length of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymer.

[8] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [7], wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F5):

nM2<nM1  (F5)

wherein nM1 is as described above, and nM2 represents an average chain length of the polyorganosiloxane blocks (A-2) in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 16,000 or more to less than 56,000 among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography.

[9] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [8], wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F6):

nM3<nM2  (F6)

wherein nM2 is as described above, and nM3 represents an average chain length of the polyorganosiloxane blocks (A-2) in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 4,500 or more to less than 16,000 among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography.

[10] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [9], wherein the polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography satisfy the following expression (F7a):

1.5≤iPOS/iPC  (F7a)

wherein iPOS represents an average content (mol) of linking groups of the polycarbonate blocks (A-1) and the polyorganosiloxane blocks (A-2), and iPC represents an average content (mol) of terminal groups of the polycarbonate blocks (A-1).

[11] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [10], wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F7b):

100<iM1/iA×100  (F7b)

wherein iM1 represents a ratio (iPOS/iPC) of iPOS to iPC in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography, and iA represents a ratio (iPOS/iPC) of iPOS to iPC in the polycarbonate-polyorganosiloxane copolymer.

[12] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [11], wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F8):

iM2<iM1  (F8)

wherein iM1 is as described above, and iM2 represents a ratio (iPOS/iPC) of iPOS to iPC in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 16,000 or more to less than 56,000 among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography.

[13] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [12], wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F9):

iM3<iM2  (F9)

wherein iM2 is as described above, and iM3 represents a ratio (iPOS/iPC) of iPOS to iPC in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 4,500 or more to less than 16,000 among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography.

[14] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [13], wherein the aromatic polycarbonate-based resin (B) contains a polycarbonate block including, in a main chain thereof, a repeating unit represented by the following general formula (III):

wherein R³⁰ and R³¹ each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X′ represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, —S—, —SO—, —SO₂—, —O—, or —CO—, and “d” and “e” each independently represent an integer of from 0 to 4.

[15] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [14], wherein the polyorganosiloxane blocks (A-2) have an average chain length of from 30 or more to 500 or less.

[16] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [15], wherein the polyorganosiloxane blocks (A-2) have an average chain length of from 55 or more to 500 or less.

[17] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [16], wherein the polyorganosiloxane blocks (A-2) have an average chain length of from 55 or more to 85 or less.

[18] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [17], wherein a content of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymer (A) is from 5 mass % or more to 70 mass % or less.

[19] The polycarbonate-polyorganosiloxane copolymer according to any one of the above-mentioned items [1] to [18], wherein the polycarbonate-polyorganosiloxane copolymer (A) has a viscosity-average molecular weight (Mv) of from 9,000 or more to 50,000 or less.

[20] A polycarbonate-based resin composition, comprising:

the polycarbonate-polyorganosiloxane copolymer (A) of any one of the above-mentioned items [1] to [19];

an aromatic polycarbonate-based resin (B) except the polycarbonate-polyorganosiloxane copolymer (A); and

a polyester-based resin (C),

wherein the polyester-based resin (C) is blended with respect to 100 parts by mass of a total of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B), and

wherein a ratio of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) in 100 mass % of a total amount of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B), and the polyester-based resin (C) is from 50 mass % or more to 99 mass % or less.

[21] The polycarbonate-based resin composition according to the above-mentioned item [20], wherein a mass ratio “(A)/(B)” of the polycarbonate-polyorganosiloxane copolymer (A) to the aromatic polycarbonate-based resin (B) is from 0.1/99.9 to 99.9/0.1.

[22] The polycarbonate-based resin composition according to the above-mentioned item [20] or [21], wherein a content of the polyorganosiloxane blocks (A-2) with respect to a total of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) is from 0.1 mass % or more to 10 mass % or less.

[23] The polycarbonate-based resin composition according to any one of the above-mentioned items [20] to [22], wherein a polycarbonate-based resin formed of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) has a viscosity-average molecular weight (Mv) of from 9,000 or more to 50,000 or less.

[24] The polycarbonate-based resin composition according to any one of the above-mentioned items [20] to [23], wherein the polyester-based resin (C) comprises at least one selected from a polyethylene terephthalate and a polybutylene terephthalate.

[25] A molded article, which is obtained by molding the polycarbonate-based resin composition of any one of the above-mentioned items [20] to [24].

[26] The molded article according to the above-mentioned item [25], wherein the molded article comprises a casing for electrical and electronic equipment.

[27] The molded article according to the above-mentioned item [25], wherein the molded article comprises a part for an automobile and a building material.

Advantageous Effects of Invention

According to the present invention, the polycarbonate-polyorganosiloxane copolymer having more excellent impact resistance, the polycarbonate-based resin composition including the polycarbonate-based resins including the polycarbonate-polyorganosiloxane copolymer and the polyester-based resin, the composition being excellent in chemical resistance, and the molded article of the composition can be obtained.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a graph in which a polycarbonate-polyorganosiloxane copolymer is fractionated into 5 fractions for respective retention times by gel permeation chromatography.

FIG. 2 is a graph showing a polyorganosiloxane block content for each molecular weight determined by the gel permeation chromatography through the use of a polycarbonate as a conversion reference in Production Example 1.

FIG. 3 is a view for illustrating an example of a linking group of a polyorganosiloxane block and a polycarbonate block, and an example of a terminal group of the polycarbonate block.

DESCRIPTION OF EMBODIMENTS

The inventors of the present invention have made extensive investigations, and as a result, have found that, when a polycarbonate-polyorganosiloxane copolymer whose polyorganosiloxane block concentration in a specific molecular weight region is equal to or more than a certain value is used, a polycarbonate-polyorganosiloxane copolymer having more excellent impact resistance is obtained without the extension of the chain length of a polyorganosiloxane block or an increase in content thereof. In addition, the inventors have found that the addition of a polyester-based resin to a polycarbonate-based resin including the polycarbonate-polyorganosiloxane copolymer provides a polycarbonate-based resin composition having excellent chemical resistance, and a molded article of the composition. Detailed description is given below.

The term “XX to YY” as used herein means “from XX or more to YY or less.” In this description, a specification considered to be preferred may be arbitrarily adopted, and a combination of preferred specifications is more preferred.

<Polycarbonate-Polyorganosiloxane Copolymer>

A polycarbonate-polyorganosiloxane copolymer according to a first embodiment of the present invention comprises: polycarbonate blocks (A-1) each formed of a repeating unit represented by the following general formula (I); and polyorganosiloxane blocks (A-2) each containing a repeating unit represented by the following general formula (II), wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F1a):

15≤wM1  (F1a)

wherein wM1 represents an average content (mass %) of the polyorganosiloxane blocks (A-2) in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using a polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among polycarbonate-polyorganosiloxane copolymers obtained through separation of the polycarbonate-polyorganosiloxane copolymer by gel permeation chromatography;

wherein R¹ and R² each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, a fluorenediyl group, an arylalkylene group having 7 to 15 carbon atoms, an arylalkylidene group having 7 to 15 carbon atoms, —S—, —SO—, —SO₂—, —O—, or —CO—, R³ and R⁴ each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and “a” and “b” each independently represent an integer of from 0 to 4.

In the general formula (I), examples of the halogen atom that R¹ and R² each independently represent include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.

Examples of the alkyl group that R¹ and R² each independently represent include a methyl group, an ethyl group, a n-propyl group, an isopropyl group, various butyl groups (the term “various” means that a linear group and all kinds of branched groups are included, and in this description, the same holds true for the following), various pentyl groups, and various hexyl groups. Examples of the alkoxy group that R¹ and R² each independently represent include alkoxy groups having the above-mentioned alkyl groups as alkyl group moieties.

Examples of the alkylene group represented by X include a methylene group, an ethylene group, a trimethylene group, a tetramethylene group, and a hexamethylene group. Among them, an alkylene group having 1 to 5 carbon atoms is preferred. Examples of the alkylidene group represented by X include an ethylidene group and an isopropylidene group. Examples of the cycloalkylene group represented by X include a cyclopentanediyl group, a cyclohexanediyl group, and a cyclooctanediyl group. Among them, a cycloalkylene group having 5 to 10 carbon atoms is preferred. Examples of the cycloalkylidene group represented by X include a cyclohexylidene group, a 3,5,5-trimethylcyclohexylidene group, and a 2-adamantylidene group. Among them, a cycloalkylidene group having 5 to 10 carbon atoms is preferred, and a cycloalkylidene group having 5 to 8 carbon atoms is more preferred. Examples of the aryl moiety of the arylalkylene group represented by X include aryl groups each having 6 to 14 ring-forming carbon atoms, such as a phenyl group, a naphthyl group, a biphenyl group, and an anthryl group, and examples of the alkylene group include the above-mentioned alkylene groups. Examples of the aryl moiety of the arylalkylidene group represented by X include aryl groups each having 6 to 14 ring-forming carbon atoms, such as a phenyl group, a naphthyl group, a biphenyl group, and an anthryl group, and examples of the alkylidene group may include the above-mentioned alkylidene groups.

“a” and “b” each independently represent an integer of from 0 to 4, preferably from 0 to 2, more preferably 0 or 1.

Among them, a repeating unit in which “a” and “b” each represent 0, and X represents a single bond or an alkylene group having 1 to 8 carbon atoms, or a repeating unit in which “a” and “b” each represent 0, and X represents an alkylene group having 3 carbon atoms, in particular an isopropylidene group is suitable.

In the general formula (II), examples of the halogen atom represented by R³ or R⁴ include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom. Examples of the alkyl group represented by R³ or R⁴ include a methyl group, an ethyl group, a n-propyl group, an isopropyl group, various butyl groups, various pentyl groups, and various hexyl groups. Examples of the alkoxy group represented by R³ or R⁴ include alkoxy groups having the above-mentioned alkyl groups as alkyl group moieties. Examples of the aryl group represented by R³ or R⁴ include a phenyl group and a naphthyl group.

R³ and R⁴ each preferably represent a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and each more preferably represent a methyl group.

More specifically, the polyorganosiloxane block (A-2) containing the repeating unit represented by the general formula (II) preferably has a unit represented by any one of the following general formulae (II-I) to (II-III):

wherein R³ to R⁶ each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and a plurality of R³, R⁴, R⁵, or R⁶ may be identical to or different from each other, Y represents —R⁷O—, —R⁷COO—, —R⁷NH—, —R⁷NR⁸—, —COO—, —S—, —R⁷COO—R⁹—O—, or —R⁷O—R¹⁰—O—, and a plurality of Ys may be identical to or different from each other, the R⁷ represents a single bond, a linear, branched, or cyclic alkylene group, an aryl-substituted alkylene group, a substituted or unsubstituted arylene group, or a diarylene group, R⁸ represents an alkyl group, an alkenyl group, an aryl group, or an aralkyl group, R⁹ represents a diarylene group, R¹⁰ represents a linear, branched, or cyclic alkylene group, or a diarylene group, β represents a divalent group derived from a diisocyanate compound, or a divalent group derived from a dicarboxylic acid or a halide of a dicarboxylic acid, “n” represents the chain length of the polyorganosiloxane, and n−1, and “p” and “q” each represent the number of repetitions of a polyorganosiloxane unit and each represent an integer of 1 or more, and the sum of “p” and “q” is n−2.

Examples of the halogen atom that R³ to R⁶ each independently represent include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom. Examples of the alkyl group that R³ to R⁶ each independently represent include a methyl group, an ethyl group, a n-propyl group, an isopropyl group, various butyl groups, various pentyl groups, and various hexyl groups. Examples of the alkoxy group that R³ to R⁶ each independently represent include alkoxy groups having the above-mentioned alkyl groups as alkyl group moieties. Examples of the aryl group that R³ to R⁶ each independently represent include a phenyl group and a naphthyl group.

R³ to R⁶ each preferably represent a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms.

R³ to R⁶ in the general formula (II-I), the general formula (II-II), and/or the general formula (II-III) each preferably represent a methyl group.

The linear or branched alkylene group represented by R⁷ in —R⁷O—, —R⁷COO—, —R⁷NH—, —R⁷NR⁸—, —R⁷COO—R⁹—O—, or —R⁷O—R¹⁰—O— represented by Y is, for example, an alkylene group having 1 to 8 carbon atoms, preferably 1 to 5 carbon atoms, and the cyclic alkylene group represented by R⁷ is, for example, a cycloalkylene group having 5 to 15 carbon atoms, preferably 5 to 10 carbon atoms.

The aryl-substituted alkylene group represented by R⁷ may have a substituent, such as an alkoxy group or an alkyl group, on its aromatic ring, and a specific structure thereof may be, for example, a structure represented by the following general formula (i) or (ii). When the block has the aryl-substituted alkylene group, the alkylene group is bonded to Si.

wherein “c” represents a positive integer and typically represents an integer of from 1 to 6.

The diarylene group represented by any one of R⁷, R⁹, and R¹⁰ refers to a group in which two arylene groups are linked to each other directly or through a divalent organic group, and is specifically a group having a structure represented by —Ar¹—W—Ar²—. Here, Ar¹ and Ar² each represent an arylene group, and W represents a single bond or a divalent organic group. Examples of the divalent organic group represented by W include an isopropylidene group, a methylene group, a dimethylene group, and a trimethylene group.

Examples of the arylene group represented by any one of R⁷, Ar¹, and Ar² include arylene groups each having 6 to 14 ring-forming carbon atoms, such as a phenylene group, a naphthylene group, a biphenylene group, and an anthrylene group. Those arylene groups may each have an arbitrary substituent, such as an alkoxy group or an alkyl group.

The alkyl group represented by R⁸ is a linear or branched group having 1 to 8, preferably 1 to 5 carbon atoms. The alkenyl group represented by R⁸ is, for example, a linear or branched group having 2 to 8, preferably 2 to 5 carbon atoms. The aryl group represented by R⁸ is, for example, a phenyl group or a naphthyl group. The aralkyl group represented by R⁸ is, for example, a phenylmethyl group or a phenylethyl group.

The linear, branched, or cyclic alkylene group represented by R¹⁰ is the same as that represented by R⁷.

Y preferably represents —R⁷O—. R⁷ preferably represents an aryl-substituted alkylene group, in particular a residue of a phenol-based compound having an alkyl group, and more preferably represents an organic residue derived from allylphenol or an organic residue derived from eugenol.

With regard to “p” and “q” in the formula (II-II), it is preferred that p=q.

In addition, β represents a divalent group derived from a diisocyanate compound, or a divalent group derived from a dicarboxylic acid or a halide of a dicarboxylic acid, and examples thereof include divalent groups represented by the following general formulae (iii) to (vii).

The average chain length “n” of the polyorganosiloxane blocks (A-2) in the PC-POS copolymer (A) is preferably 30 or more, more preferably 35 or more, still more preferably 40 or more, still further more preferably 50 or more, particularly preferably 55 or more, most preferably 60 or more. In addition, the average chain length is preferably 500 or less, more preferably 400 or less, still more preferably 300 or less, still further more preferably 200 or less, particularly preferably 120 or less, most preferably 85 or less. The average chain length is calculated by nuclear magnetic resonance (NMR) measurement. When the average chain length “n” falls within the range of from 30 or more to 500 or less, more excellent impact resistance can be obtained. In addition, the average chain length “n” of the polyorganosiloxane blocks (A-2) preferably falls within the range of from 55 or more to 500 or less from the viewpoint that more excellent impact resistance is obtained.

The content of the polyorganosiloxane blocks (A-2) in the PC-POS copolymer (A) is preferably 5 mass % or more, more preferably 6 mass % or more, still more preferably 10 mass % or more, still further more preferably 14 mass % or more, still further more preferably 18 mass % or more, particularly preferably 21 mass % or more, and is preferably 70 mass % or less, more preferably 50 mass % or less, still more preferably 45 mass % or less, particularly preferably 40 mass % or less. When the content of the polyorganosiloxane blocks in the PC-POS copolymer (A) falls within the range, more excellent impact resistance can be obtained.

The viscosity-average molecular weight (Mv) of the PC-POS copolymer (A) may be appropriately adjusted by using, for example, a molecular weight modifier (terminal stopper) so as to be a target molecular weight in accordance with applications or products in which the copolymer is used. However, the viscosity-average molecular weight is preferably 9,000 or more, more preferably 12,000 or more, still more preferably 14,000 or more, particularly preferably 16,000 or more, and is preferably 50,000 or less, more preferably 30,000 or less, still more preferably 23,000 or less, particularly preferably 22,000 or less, most preferably 20,000 or less. When the viscosity-average molecular weight is 9,000 or more, a sufficient strength of a molded article can be obtained. When the viscosity-average molecular weight is 50,000 or less, injection molding or extrusion molding can be performed at the temperature at which the heat deterioration of the copolymer does not occur.

The viscosity-average molecular weight (Mv) is a value calculated from the following Schnell's equation by measuring the limiting viscosity [η] of a methylene chloride solution at 20° C.

[η]=1.23×10⁻⁵ ×Mv ^(0.83)

The polycarbonate-polyorganosiloxane copolymer (A) may be produced by a known production method, such as an interfacial polymerization method (phosgene method), a pyridine method, or an ester exchange method. Particularly in the case of the interfacial polymerization method, a step of separating an organic phase containing the PC-POS copolymer (A) and an aqueous phase containing an unreacted product, a catalyst residue, or the like becomes easier, and hence the separation of the organic phase containing the PC-POS copolymer (A) and the aqueous phase in each washing step based on alkali washing, acid washing, or pure water washing becomes easier. Accordingly, the PC-POS copolymer (A) is efficiently obtained. With regard to a method of producing the PC-POS copolymer (A), reference may be made to, for example, a method described in JP 2010-241943 A.

Specifically, the PC-POS copolymer (A) may be produced by: dissolving a polycarbonate oligomer produced in advance to be described later and a polyorganosiloxane in a water-insoluble organic solvent (e.g., methylene chloride); adding a solution of a dihydric phenol-based compound (e.g., bisphenol A) in an aqueous alkali compound (e.g., aqueous sodium hydroxide) to the solution; and subjecting the mixture to an interfacial polycondensation reaction through the use of a tertiary amine (e.g., triethylamine) or a quaternary ammonium salt (e.g., trimethylbenzylammonium chloride) as a polymerization catalyst in the presence of a terminal stopper (a monohydric phenol, such as p-tert-butylphenol). In addition, the PC-POS copolymer (A) may also be produced by copolymerizing the polyorganosiloxane and a dihydric phenol, and phosgene, a carbonate ester, or a chloroformate.

When the polycarbonate-polyorganosiloxane copolymer (A) in the polycarbonate-based resin composition of the present application is produced by, for example, causing the polycarbonate oligomer and a polyorganosiloxane raw material to react with each other in an organic solvent, and then causing the resultant to react with the dihydric phenol, the solid content weight (g/L) of the polycarbonate oligomer in 1 L of a mixed solution of the organic solvent and the polycarbonate oligomer preferably falls within the range of from 80 g/L or more to 200 g/L or less. The solid content weight is more preferably 90 g/L or more, still more preferably 100 g/L or more, and is more preferably 180 g/L or less, still more preferably 170 g/L or less.

A polyorganosiloxane represented by the following general formula (1), general formula (2), and/or general formula (3) may be used as the polyorganosiloxane serving as a raw material:

wherein

R³ to R⁶, Y, β, n−1, “p”, and “q” are as described above, and specific examples and preferred examples thereof are also the same as those described above, and

Z represents a hydrogen atom or a halogen atom, and a plurality of Z may be identical to or different from each other.

Examples of the polyorganosiloxane represented by the general formula (1) include compounds each represented by any one of the following general formulae (1-1) to (1-11):

wherein in the general formulae (1-1) to (1-11), R³ to R⁶, “n”, and R⁸ are as defined above, and preferred examples thereof are also the same as those described above, and “c” represents a positive integer and typically represents an integer of from 1 to 6.

Among them, a phenol-modified polyorganosiloxane represented by the general formula (1-1) is preferred from the viewpoint of its ease of polymerization. In addition, an α,ω-bis[3-(o-hydroxyphenyl)propyl]polydimethylsiloxane, which is one compound represented by the general formula (1-2), or an α,ω-bis[3-(4-hydroxy-3-methoxyphenyl)propyl]polydimethylsiloxane, which is one compound represented by the general formula (1-3), is preferred from the viewpoint of its ease of availability.

In addition to the foregoing, a compound having a structure represented by the following general formula (4) may be used as a polyorganosiloxane raw material:

wherein R³ and R⁴ are identical to those described above. The average chain length of the polyorganosiloxane block represented by the general formula (4) is (r×m), and the range of the (r×m) is the same as that of the “n”.

When the compound represented by the general formula (4) is used as a polyorganosiloxane raw material, the polyorganosiloxane block (A-2) preferably has a unit represented by the following general formula (II-IV):

wherein R³, R⁴, “r”, and “m” are as described above.

The copolymer may include a structure represented by the following general formula (II-V) as the polyorganosiloxane block (A-2):

wherein R¹⁸ to R²¹ each independently represent a hydrogen atom or an alkyl group having 1 to 13 carbon atoms, R²² represents an alkyl group having 1 to 6 carbon atoms, a hydrogen atom, a halogen atom, a hydroxy group, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 14 carbon atoms, Q² represents a divalent aliphatic group having 1 to 10 carbon atoms, and “n” represents an average chain length and represents from 30 to 70.

In the general formula (II-V), examples of the alkyl group having 1 to 13 carbon atoms that R¹⁸ to R²¹ each independently represent include a methyl group, an ethyl group, a n-propyl group, an isopropyl group, various butyl groups, various pentyl groups, various hexyl groups, various heptyl groups, various octyl groups, a 2-ethylhexyl group, various nonyl groups, various decyl groups, various undecyl groups, various dodecyl groups, and various tridecyl groups. Among them, R¹⁸ to R²¹ each preferably represent a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, and it is more preferred that all of R¹⁸ to R²¹ each represent a methyl group.

Examples of the alkyl group having 1 to 6 carbon atoms represented by R²² include a methyl group, an ethyl group, a n-propyl group, an isopropyl group, various butyl groups, various pentyl groups, and various hexyl groups. Examples of the halogen atom represented by R²² include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom. An example of the alkoxy group having 1 to 6 carbon atoms represented by R²² is an alkoxy group whose alkyl group moiety is the alkyl group described above. In addition, examples of the aryl group having 6 to 14 carbon atoms represented by R²² include a phenyl group, a toluyl group, a dimethylphenyl group, and a naphthyl group.

Among them, R²² preferably represents a hydrogen atom or an alkoxy group having 1 to 6 carbon atoms, more preferably represents a hydrogen atom or an alkoxy group having 1 to 3 carbon atoms, and still more preferably represents a hydrogen atom.

The divalent aliphatic group having 1 to 10 carbon atoms represented by Q² is preferably a linear or branched divalent saturated aliphatic group having 1 to 10 carbon atoms. The number of carbon atoms of the saturated aliphatic group is preferably from 1 to 8, more preferably from 2 to 6, still more preferably from 3 to 6, still further more preferably from 4 to 6. In addition, the average chain length “n” is as described above.

A preferred mode of the constituent unit (II-V) may be, for example, a structure represented by the following general formula (II-VI):

wherein “n” is identical to that described above.

The polyorganosiloxane block (A-2) represented by the general formula (II-V) or (II-VI) may be obtained by using a polyorganosiloxane raw material represented by the following general formula (5) or (6):

wherein R¹⁸ to R²², Q², and “n” are as described above;

wherein “n” is as described above.

A method of producing the polyorganosiloxane is not particularly limited. According to, for example, a method described in JP 11-217390 A, a crude polyorganosiloxane may be obtained by: causing cyclotrisiloxane and disiloxane to react with each other in the presence of an acid catalyst to synthesize α,ω-dihydrogen organopentasiloxane; and then subjecting the α,ω-dihydrogen organopentasiloxane to an addition reaction with, for example, a phenolic compound (e.g., 2-allylphenol, 4-allylphenol, eugenol, or 2-propenylphenol) in the presence of a catalyst for a hydrosilylation reaction. In addition, according to a method described in JP 2662310 B2, the crude polyorganosiloxane may be obtained by: causing octamethylcyclotetrasiloxane and tetramethyldisiloxane to react with each other in the presence of sulfuric acid (acid catalyst); and subjecting the resultant α,ω-dihydrogen organopolysiloxane to an addition reaction with the phenolic compound or the like in the presence of the catalyst for a hydrosilylation reaction in the same manner as that described above. The α,ω-dihydrogen organopolysiloxane may be used after its chain length “n” has been appropriately adjusted in accordance with its polymerization conditions, or a commercial α,ω-dihydrogen organopolysiloxane may be used.

Examples of the catalyst for a hydrosilylation reaction include transition metal-based catalysts. Among them, a platinum-based catalyst is preferably used in terms of a reaction rate and selectivity. Specific examples of the platinum-based catalyst include chloroplatinic acid, an alcohol solution of chloroplatinic acid, an olefin complex of platinum, a complex of platinum and a vinyl group-containing siloxane, platinum-supported silica, and platinum-supported activated carbon.

The crude polyorganosiloxane is preferably brought into contact with an adsorbent to cause the adsorbent to adsorb and remove a transition metal derived from a transition metal-based catalyst in the crude polyorganosiloxane, the catalyst having been used as the catalyst for a hydrosilylation reaction.

An adsorbent having an average pore diameter of, for example, 1,000 Å or less may be used as the adsorbent. When the average pore diameter is 1,000 Å or less, the transition metal in the crude polyorganosiloxane can be efficiently removed. From such viewpoint, the average pore diameter of the adsorbent is preferably 500 Å or less, more preferably 200 Å or less, still more preferably 150 Å or less, still further more preferably 100 Å or less. In addition, from the same viewpoint, the adsorbent is preferably a porous adsorbent.

Although the adsorbent is not particularly limited as long as the adsorbent has the above-mentioned average pore diameter, for example, activated clay, acid clay, activated carbon, synthetic zeolite, natural zeolite, activated alumina, silica, a silica-magnesia-based adsorbent, diatomaceous earth, or cellulose may be used, and at least one selected from the group consisting of activated clay, acid clay, activated carbon, synthetic zeolite, natural zeolite, activated alumina, silica, and a silica-magnesia-based adsorbent is preferred.

After the adsorbent has been caused to adsorb the transition metal in the crude polyorganosiloxane, the adsorbent may be separated from the polyorganosiloxane by arbitrary separating means. Examples of the means for separating the adsorbent from the polyorganosiloxane include a filter and centrifugal separation. When the filter is used, a filter such as a membrane filter, a sintered metal filter, or a glass fiber filter may be used. Among them, a membrane filter is particularly preferably used.

The average particle diameter of the adsorbent is typically from 1 μm or more to 4 mm or less, preferably from 1 μm or more to 100 μm or less from the viewpoint that the adsorbent is separated from the polyorganosiloxane after the adsorption of the transition metal.

When the adsorbent is used, its usage amount is not particularly limited. The porous adsorbent may be used in an amount in the range of from preferably 1 part by mass or more, more preferably 2 parts by mass or more to preferably 30 parts by mass or less, more preferably 20 parts by mass or less with respect to 100 parts by mass of the crude polyorganosiloxane.

When the crude polyorganosiloxane to be treated has so high a molecular weight that the polyorganosiloxane is not in a liquid state, the polyorganosiloxane may be heated to such a temperature as to be in a liquid state at the time of the performance of the adsorption with the adsorbent and the separation of the adsorbent. Alternatively, the adsorption and the separation may be performed after the polyorganosiloxane has been dissolved in a solvent, such as methylene chloride or hexane.

A polyorganosiloxane having a desired molecular weight distribution is obtained by regulating its molecular weight distribution through, for example, the blending of a plurality of polyorganosiloxanes. With regard to the blending, a crude polyorganosiloxane having a desired molecular weight distribution may be obtained by blending a plurality of α,ω-dihydrogen organopolysiloxanes and then subjecting a phenolic compound or the like to an addition reaction with the resultant in the presence of a catalyst for a hydrosilylation reaction. Purification, such as the removal of the catalyst for a hydrosilylation reaction, may be performed after a plurality of crude polyorganosiloxanes have been blended. A plurality of polyorganosiloxanes after the purification may be blended. In addition, a molecular weight distribution may be appropriately adjusted depending on a polymerization condition at the time of the production of a polyorganosiloxane. Further, a desired molecular weight distribution may be obtained by fractionating only part of existing polyorganosiloxanes through means such as various kinds of separation.

The polycarbonate oligomer may be produced by a reaction between a dihydric phenol and a carbonate precursor, such as phosgene or triphosgene, in an organic solvent, such as methylene chloride, chlorobenzene, or chloroform. When the polycarbonate oligomer is produced by using an ester exchange method, the oligomer may be produced by a reaction between the dihydric phenol and a carbonate precursor, such as diphenyl carbonate.

A dihydric phenol represented by the following general formula (viii) is preferably used as the dihydric phenol:

wherein R¹, R², “a”, “b”, and X are as described above.

Examples of the dihydric phenol represented by the general formula (viii) include: bis(hydroxyphenyl)alkane-based dihydric phenols, such as 2,2-bis(4-hydroxyphenyl)propane [bisphenol A], bis(4-hydroxyphenyl)methane, 1,1-bis(4-hydroxyphenyl) ethane, and 2,2-bis(4-hydroxy-3,5-dimethylphenyl)propane; 4,4′-dihydroxydiphenyl; bis(4-hydroxyphenyl)cycloalkanes; bis(4-hydroxyphenyl) oxide; bis(4-hydroxyphenyl) sulfide; bis(4-hydroxyphenyl) sulfone; bis(4-hydroxyphenyl) sulfoxide; and bis(4-hydroxyphenyl) ketone. Those dihydric phenols may be used alone or as a mixture thereof.

Among them, bis(hydroxyphenyl)alkane-based dihydric phenols are preferred, and bisphenol A is more preferred. When bisphenol A is used as the dihydric phenol, the PC-POS copolymer is such that in the general formula (i), X represents an isopropylidene group and a=b=0.

Examples of the dihydric phenol except bisphenol A include bis(hydroxyaryl)alkanes, bis(hydroxyaryl)cycloalkanes, dihydroxyaryl ethers, dihydroxydiaryl sulfides, dihydroxydiaryl sulfoxides, dihydroxydiaryl sulfones, dihydroxydiphenyls, dihydroxydiaryl fluorenes, and dihydroxydiaryl adamantanes. Those dihydric phenols may be used alone or as a mixture thereof.

Examples of the bis(hydroxyaryl)alkanes include bis(4-hydroxyphenyl)methane, 1,1-bis(4-hydroxyphenyl)ethane, 2,2-bis(4-hydroxyphenyl)butane, 2,2-bis(4-hydroxyphenyl)octane, bis(4-hydroxyphenyl)phenylmethane, bis(4-hydroxyphenyl)diphenylmethane, 2,2-bis(4-hydroxy-3-methylphenyl)propane, bis(4-hydroxyphenyl)naphthylmethane, 1,1-bis(4-hydroxy-3-tert-butylphenyl)propane, 2,2-bis(4-hydroxy-3-bromophenyl)propane, 2,2-bis(4-hydroxy-3,5-dimethylphenyl)propane, 2,2-bis(4-hydroxy-3-chlorophenyl)propane, 2,2-bis(4-hydroxy-3,5-dichlorophenyl)propane, and 2,2-bis(4-hydroxy-3,5-dibromophenyl)propane.

Examples of the bis(hydroxyaryl)cycloalkanes include 1,1-bis(4-hydroxyphenyl)cyclopentane, 1,1-bis(4-hydroxyphenyl)cyclohexane, 1,1-bis(4-hydroxyphenyl)-3,5,5-trimethylcyclohexane, 2,2-bis(4-hydroxyphenyl)norbornane, and 1,1-bis(4-hydroxyphenyl)cyclododecane. Examples of the dihydroxyaryl ethers include 4,4′-dihydroxydiphenyl ether and 4,4′-dihydroxy-3,3′-dimethylphenyl ether.

Examples of the dihydroxydiaryl sulfides include 4,4′-dihydroxydiphenyl sulfide and 4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfide. Examples of the dihydroxydiaryl sulfoxides include 4,4′-dihydroxydiphenyl sulfoxide and 4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfoxide. Examples of the dihydroxydiaryl sulfones include 4,4′-dihydroxydiphenyl sulfone and 4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfone.

An example of the dihydroxydiphenyls is 4,4′-dihydroxydiphenyl. Examples of the dihydroxydiarylfluorenes include 9,9-bis(4-hydroxyphenyl)fluorene and 9,9-bis(4-hydroxy-3-methylphenyl)fluorene. Examples of the dihydroxydiaryladamantanes include 1,3-bis(4-hydroxyphenyl)adamantane, 2,2-bis(4-hydroxyphenyl)adamantane, and 1,3-bis(4-hydroxyphenyl)-5,7-dimethyladamantane.

Examples of dihydric phenols except those described above include 4,4′-[1,3-phenylenebis(1-methylethylidene)]bisphenol, 10,10-bis(4-hydroxyphenyl)-9-anthrone, and 1,5-bis(4-hydroxyphenylthio)-2,3-dioxapentane.

In order to adjust the molecular weight of the PC-POS copolymer to be obtained, a terminal stopper (molecular weight modifier) may be used. Examples of the terminal stopper may include monohydric phenols, such as phenol, p-cresol, p-tert-butylphenol, p-tert-octylphenol, p-cumylphenol, p-nonylphenol, m-pentadecylphenol, and p-tert-amylphenol. Those monohydric phenols may be used alone or in combination thereof.

After the interfacial polycondensation reaction, the PC-POS copolymer (A) may be obtained by appropriately leaving the resultant at rest to separate the resultant into an aqueous phase and an organic solvent phase [separating step], washing the organic solvent phase (preferably washing the phase with a basic aqueous solution, an acidic aqueous solution, and water in the stated order) [washing step], concentrating the resultant organic phase [concentrating step], and drying the concentrated phase [drying step].

The polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer in the first embodiment of the present invention by gel permeation chromatography are required to satisfy the expression (F1a):

15≤wM1  (F1a)

wherein wM1 represents the average content (mass %) of the polyorganosiloxane blocks (A-2) in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using a polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among polycarbonate-polyorganosiloxane copolymers obtained through separation of the polycarbonate-polyorganosiloxane copolymer by gel permeation chromatography.

Specifically, the average content of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among the polycarbonate-polyorganosiloxane copolymers obtained through the separation by the gel permeation chromatography is 15 mass % or more, preferably 20 mass % or more, more preferably 30 mass % or more, still more preferably 40 mass % or more from the viewpoint of the impact resistance of the copolymer.

In addition, the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the above-mentioned polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography more desirably satisfy the following expression (F1a′):

13≤wM2  (F1a′)

wherein wM2 represents the average content (mass %) of the polyorganosiloxane blocks (A-2) in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 16,000 or more to less than 56,000 among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography.

Specifically, the average content of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 16,000 or more to less than 56,000 among the polycarbonate-polyorganosiloxane copolymers obtained through the separation by the gel permeation chromatography is preferably 13 mass % or more, more preferably 18 mass % or more, still more preferably 22 mass % or more, particularly preferably 27 mass % or more from the viewpoint of the impact resistance.

In addition, the average content (wA) of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymer, and the average content (wM1) of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography preferably satisfy the following expression (F1b):

100<wM1/wA×100  (F1b)

wherein wM1 is as described above, and wA represents the average content (mass %) of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymer. The value of wM1/wA×100 is more preferably 115 or more, still more preferably 130 or more, still further more preferably 145 or more, particularly preferably 160 or more.

When the value of the wM1/wA×100 falls within the range, a large amount of the polyorganosiloxane blocks (A-2) are unevenly distributed in polycarbonate-polyorganosiloxane copolymers each having a higher molecular weight, and hence the impact resistance can be efficiently improved with respect to the average content of the polyorganosiloxane blocks (A-2) in the entirety of the polycarbonate-polyorganosiloxane copolymer.

Further, polycarbonate-polyorganosiloxane copolymers each having a higher molecular weight determined by using the polycarbonate as a conversion reference among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography preferably have a higher average content of the polyorganosiloxane blocks (A-2). Specifically, the polycarbonate-polyorganosiloxane copolymer preferably satisfies the following expression (F2) and/or the following expression (F3):

wM2<wM1  (F2)

wherein wM1 and wM2 are as described above;

wM3<wM2  (F3)

wherein wM2 is as described above, and wM3 represents the average content (mass %) of the polyorganosiloxane blocks (A-2) in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 4,500 or more to less than 16,000 among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography.

The expression (F2) means that the average content (wM1) of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight of from 56,000 or more to 200,000 or less is larger than the average content (wM2) in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight of from 16,000 or more to less than 56,000. The expression (F3) means that the average content (wM2) of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight of from 16,000 or more to less than 56,000 is larger than the average content (wM3) in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight of from 4,500 or more to less than 16,000.

The polycarbonate-polyorganosiloxane copolymer preferably satisfies the expression (F2) and/or the expression (F3) because a larger amount of the polyorganosiloxane blocks (A-2) are unevenly distributed in polycarbonate-polyorganosiloxane copolymers each having a higher molecular weight, and hence the impact resistance can be more efficiently improved with respect to the average content of the polyorganosiloxane blocks (A-2) in the entirety of the polycarbonate-polyorganosiloxane copolymer.

The average chain length of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography preferably satisfies the following expression (F4a) from the viewpoint that higher impact resistance is obtained:

50≤nM1  (F4a)

wherein nM1 represents the average chain length of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography.

The nM1 is preferably 50 or more, more preferably 60 or more, still more preferably 70 or more.

In addition, the average chain length (nA) of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymer, and the average chain length (nM1) of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography preferably satisfy the following expression (F4b):

100<nM1/nA×100  (F4b)

wherein the value of nM1/nA×100 is preferably more than 100, more preferably 105 or more, still more preferably 110 or more, still further more preferably 115 or more, particularly preferably 120 or more.

When the value of the nM1/nA×100 falls within the range, a large amount of the polyorganosiloxane blocks (A-2) each having a longer chain length are unevenly distributed in polycarbonate-polyorganosiloxane copolymers each having a higher molecular weight, and hence the impact resistance can be efficiently improved with respect to the average chain length of the polyorganosiloxane blocks (A-2) in the entirety of the polycarbonate-polyorganosiloxane copolymer.

Further, polycarbonate-polyorganosiloxane copolymers each having a higher molecular weight determined by using the polycarbonate as a conversion reference among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography preferably have a longer average chain length of the polyorganosiloxane blocks (A-2).

Specifically, the copolymer preferably satisfies the following expression (F5) and/or the following expression (F6):

nM2<nM1  (F5)

wherein nM2 represents the average chain length of the polyorganosiloxane blocks (A-2) in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 16,000 or more to less than 56,000 among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography;

nM3<nM2  (F6)

wherein nM3 represents the average chain length of the polyorganosiloxane blocks (A-2) in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 4,500 or more to less than 16,000 among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography.

According to the expression (F5), the average chain length of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 16,000 or more to less than 56,000 among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography is preferably shorter than the average chain length of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight of from 56,000 or more to 200,000 or less.

According to the expression (F6), the average chain length of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 4,500 or more to less than 16,000 among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography is preferably shorter than the average chain length of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight of from 16,000 or more to less than 56,000.

That is, a large amount of the polyorganosiloxane blocks (A-2) each having a longer chain length are unevenly distributed in polycarbonate-polyorganosiloxane copolymers each having a higher molecular weight. Accordingly, the impact resistance can be more efficiently improved with respect to the average chain length of the polyorganosiloxane blocks (A-2) in the entirety of the polycarbonate-polyorganosiloxane copolymer.

The polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography preferably satisfy the following expression (F7a):

1.5≤iPOS/iPC  (F7a)

wherein iPOS represents the average content (mol) of linking groups of the polycarbonate blocks (A-1) and the polyorganosiloxane blocks (A-2), and iPC represents the average content (mol) of terminal groups of the polycarbonate blocks (A-1).

In addition, iA (iPOS/iPC) serving as the ratio of iPOS to iPC in the polycarbonate-polyorganosiloxane copolymer, and iM1 (iPOS/iPC) serving as the ratio of iPOS to iPC in the polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography preferably satisfy the following expression (F7b):

100<iM1/iA×100  (F7b)

wherein the value of iM1/iA×100 is preferably more than 100, more preferably 130 or more, still more preferably 150 or more, still further more preferably 200 or more, particularly preferably 250 or more.

When the value of the iM1/iA×100 falls within the range, a large amount of molecular chains formed of the polyorganosiloxane blocks (A-2) are unevenly distributed in polycarbonate-polyorganosiloxane copolymers each having a higher molecular weight, and hence the impact resistance can be efficiently improved with respect to the average number of the molecular chains formed of the polyorganosiloxane blocks (A-2) in the entirety of the polycarbonate-polyorganosiloxane copolymer.

Further, polycarbonate-polyorganosiloxane copolymers each having a higher molecular weight determined by using the polycarbonate as a conversion reference among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography preferably have a higher value of the iPOS/iPC.

Specifically, the polycarbonate-polyorganosiloxane copolymer preferably satisfies the following expression (F8) and/or the following expression (F9):

iM2<iM1  (F8)

wherein iM1 is as described above, and iM2 represents the ratio (iPOS/iPC) of iPOS to iPC in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 16,000 or more to less than 56,000 among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography;

iM3<iM2  (F9)

wherein iM2 is as described above, and iM3 represents the ratio (iPOS/iPC) of iPOS to iPC in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using the polycarbonate as a conversion reference of from 4,500 or more to less than 16,000 among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography.

The polycarbonate-polyorganosiloxane copolymer preferably satisfies the expression (F8) and/or the expression (F9) because a larger amount of molecular chains formed of the polyorganosiloxane blocks (A-2) are unevenly distributed in polycarbonate-polyorganosiloxane copolymers each having a higher molecular weight among the polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by the gel permeation chromatography, and hence the impact resistance can be more efficiently improved with respect to the average number of the molecular chains formed of the polyorganosiloxane blocks (A-2) in the entirety of the polycarbonate-polyorganosiloxane copolymer.

<Polycarbonate-Based Resin Composition>

A polycarbonate-based resin composition according to a second embodiment of the present invention comprises: the polycarbonate-polyorganosiloxane copolymer (A); an aromatic polycarbonate-based resin (B) except the polycarbonate-polyorganosiloxane copolymer (A); and a polyester-based resin (C), wherein the polyester-based resin (C) is blended with respect to 100 parts by mass of a total of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B), and wherein a ratio of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) in 100 mass % of a total amount of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B), and the polyester-based resin (C) is from 50 mass % or more to 99 mass % or less:

wherein R¹ and R² each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, a fluorenediyl group, an arylalkylene group having 7 to 15 carbon atoms, an arylalkylidene group having 7 to 15 carbon atoms, —S—, —SO—, —SO₂—, —O—, or —CO—, R³ and R⁴ each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and “a” and “b” each independently represent an integer of from 0 to 4.

In the polycarbonate-based resin composition, the content of the polycarbonate-polyorganosiloxane copolymer (A) in the total amount of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) is typically 0.1 mass % or more, preferably 1 mass % or more, more preferably 3 mass % or more, still more preferably 10 mass % or more, and is typically 99.9 mass % or less, preferably 99 mass % or less, more preferably 30 mass % or less, still more preferably 25 mass % or less, particularly preferably 20 mass % or less, most preferably 16 mass % or less from the viewpoint that a resin composition having desired properties, such as impact resistance and chemical resistance, is obtained.

The content of the aromatic polycarbonate-based resin (B) with respect to the total amount of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) is typically 0.1 mass % or more, preferably 1 mass % or more, more preferably 50 mass % or more, still more preferably 80 mass % or more, and is typically 99.9 mass % or less, preferably 99 mass % or less, more preferably 98 mass % or less, still more preferably 95 mass % or less, particularly preferably 90 mass % or less from the viewpoint of the impact resistance of the resin composition to be obtained.

In one aspect of this embodiment, the total amount of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) is 100 mass %.

In this embodiment, the mass ratio “(A)/(B)” of the polycarbonate-polyorganosiloxane copolymer (A) to the aromatic polycarbonate-based resin (B) is typically from 0.1/99.9 to 99.9/0.1, preferably from 1/99 to 99/1, more preferably from 2/98 to 50/50, still more preferably from 5/95 to 20/80 from the viewpoint of the impact resistance of the resin composition to be obtained.

The content of the polyorganosiloxane blocks (A-2) in a polycarbonate-based resin formed of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) is preferably 0.1 mass % or more, more preferably 0.4 mass % or more, still more preferably 0.8 mass % or more, still further more preferably 1 mass % or more, particularly preferably 3 mass % or more, and is preferably 10 mass % or less, more preferably 7 mass % or less, still more preferably 6 mass % or less, particularly preferably 5 mass % or less, most preferably 4 mass % or less. When the content of the polyorganosiloxane blocks (A-2) in the polycarbonate-based resin falls within the range, an excellent impact-resisting characteristic can be obtained.

The viscosity-average molecular weight (Mv) of the polycarbonate-based resin formed of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) may be appropriately adjusted by using, for example, a molecular weight modifier (terminal stopper) so as to be a target molecular weight in accordance with applications or products in which the polycarbonate-based resin is used. The viscosity-average molecular weight of the polycarbonate-based resin formed of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) is preferably 9,000 or more, more preferably 12,000 or more, still more preferably 14,000 or more, particularly preferably 16,000 or more, and is preferably 50,000 or less, more preferably 30,000 or less, still more preferably 23,000 or less, particularly preferably 21,000 or less. When the viscosity-average molecular weight is 9,000 or more, a sufficient strength of a molded article can be obtained. When the viscosity-average molecular weight is 50,000 or less, injection molding or extrusion molding can be performed at the temperature at which the heat deterioration of the polycarbonate-based resin does not occur.

The viscosity-average molecular weight (Mv) is a value calculated from the following Schnell's equation by measuring the limiting viscosity [r] of a methylene chloride solution at 20° C.

[η]=1.23×10⁻⁵ ×Mv ^(0.83)

<(B) Aromatic Polycarbonate-Based Resin>

The aromatic polycarbonate-based resin (B) except the polycarbonate-polyorganosiloxane copolymer (A) includes, in a main chain thereof, a repeating unit represented by the following general formula (III). The polycarbonate-based resin is not particularly limited, and various known polycarbonate-based resins may each be used.

wherein R³⁰ and R³¹ each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X′ represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, —S—, —SO—, —SO₂—, —O—, or —CO—, and “d” and “e” each independently represent an integer of from 0 to 4.

Specific examples of R³⁰ and R³¹ include the same examples as those of R¹ and R², and preferred examples thereof are also the same as those of R¹ and R². R³⁰ and R³¹ each more preferably represent an alkyl group having 1 to 6 carbon atoms or an alkoxy group having 1 to 6 carbon atoms. Specific examples of X′ include the same examples as those of X, and preferred examples thereof are also the same as those of X. “d” and “e” each independently represent preferably from 0 to 2, more preferably 0 or 1.

Specifically, a resin obtained by a conventional production method for a polycarbonate may be used as the aromatic polycarbonate-based resin (B). Examples of the conventional method include: an interfacial polymerization method involving causing the dihydric phenol-based compound and phosgene to react with each other in the presence of an organic solvent inert to the reaction and an aqueous alkali solution, adding a polymerization catalyst, such as a tertiary amine or a quaternary ammonium salt, to the resultant, and polymerizing the mixture; and a pyridine method involving dissolving the dihydric phenol-based compound in pyridine or a mixed solution of pyridine and an inert solvent, and introducing phosgene to the solution to directly produce the resin.

A molecular weight modifier (terminal stopper), a branching agent, or the like is used as required in the reaction.

The dihydric phenol-based compound is, for example, a compound represented by the following general formula (III′):

wherein R³⁰, R³¹, X′, “d”, and “e” are as defined above, and preferred examples thereof are also the same as those described above.

Specific examples of the dihydric phenol-based compound may include those described above in the method of producing the polycarbonate-polyorganosiloxane copolymer (A), and preferred examples thereof are also the same as those described above. Among them, bis(hydroxyphenyl)alkane-based dihydric phenols are preferred, and bisphenol A is more preferred.

The aromatic polycarbonate-based resins may be used alone or in combination thereof. The aromatic polycarbonate resin (B) may have a structure free of such a polyorganosiloxane block as represented by the formula (II) unlike the polycarbonate-polyorganosiloxane copolymer (A). For example, the aromatic polycarbonate-based resin (B) may be a homopolycarbonate resin.

<Polyester-Based Resin (C)>

The polyester-based resin (C) to be used in the polycarbonate-based resin composition of the present invention is a polymer or copolymer obtained by a condensation reaction involving using an aromatic dicarboxylic acid or a reactive derivative thereof and a diol or an ester derivative thereof as main components.

Examples of the aromatic dicarboxylic acid include terephthalic acid, isophthalic acid, o-phthalic acid, 1,5-naphthalenedicarboxylic acid, 2,6-naphthalenedicarboxylic acid, 4,4′-biphenyldicarboxylic acid, 4,4′-biphenyl ether dicarboxylic acid, 4,4′-biphenylmethane dicarboxylic acid, 4,4′-biphenyl sulfone dicarboxylic acid, 4,4′-biphenylisopropylidene dicarboxylic acid, 1,2-bis(phenoxy)ethane-4,4′-dicarboxylic acid, 2,5-anthracenedicarboxylic acid, 2,6-anthracenedicarboxylic acid, 4,4′-p-terphenylenedicarboxylic acid, and 2,5-pyridinedicarboxylic acid. Substituted products (e.g., alkyl group-substituted products, such as 5-methylisophthalic acid) and reactive derivatives (e.g., alkyl ester derivatives, such as dimethyl terephthalate and diethyl terephthalate) thereof may also be used.

Among them, terephthalic acid and 2,6-naphthalenedicarboxylic acid, and alkyl ester derivatives thereof are more preferred, and terephthalic acid and alkyl ester derivatives thereof are particularly preferred. Those aromatic dicarboxylic acids may be used alone or in combination thereof. One or more of, for example, aliphatic dicarboxylic acids, such as adipic acid, azelaic acid, sebacic acid, and dodecanedioic acid, and alicyclic dicarboxylic acids, such as cyclohexane dicarboxylic acid, may also be used in combination with the aromatic dicarboxylic acid.

Examples of the diols each serving as a component of the polyester-based resin (C) may include: aliphatic diols, such as ethylene glycol, diethylene glycol, 1,2-propylene glycol, 1,3-propanediol, triethylene glycol, 1,4-butanediol, neopentyl glycol, 1,5-pentanediol, 1,6-hexanediol, decamethylene glycol, and 2,2-dimethyl-1,3-propanediol; alicyclic diols, such as 1,4-cyclohexanedimethanol, 1,3-cyclohexanedimethanol, cyclohexanediol, and trans- or cis-2,2,4,4-tetramethyl-1,3-cyclobutanediol; and aromatic diols, such as p-xylenediol, bisphenol A, tetrabromobisphenol A, and tetrabromobisphenol A-bis(2-hydroxyethyl ether). Substituted products thereof may also be used.

Among them, in terms of heat resistance, dimensional stability, and the like, an aliphatic diol is preferred, ethylene glycol, 1,4-butanediol, or 1,4-cyclohexanedimethanol is more preferred, and ethylene glycol is particularly preferred. The diols may be used alone or in combination thereof. In addition, one or more of long-chain diols each having a molecular weight of from 400 to 6,000, that is, for example, a polyethylene glycol, a poly-1,3-propylene glycol, and a polytetramethylene glycol may be used as diol components in combination with the above-mentioned diols and copolymerized therewith.

The polyester-based resin (C) may be copolymerized with a hydroxycarboxylic acid, such as parahydroxybenzoic acid, any other carboxylic acid, or an alcohol except the above-mentioned diols, and such copolymerized resin may also be used in the present invention. However, the amount of such copolymerized component is preferably as small as possible, and components derived from the aromatic dicarboxylic acid and the aliphatic diol account for preferably 80 mass % or more, more preferably 90 mass % or more of the polyester-based resin (C). In addition, one kind of compound accounts for preferably 80 mol % or more, more preferably 90 mol % or more of each of the aromatic dicarboxylic acid and the aliphatic diol.

The polyester-based resin (C) may be branched by introducing a small amount of a branching agent. Although the kind of the branching agent is not limited, examples thereof include trimesic acid, trimellitic acid, trimethylolethane, trimethylolpropane, and pentaerythritol.

Specific examples of the polyester-based resin (C) include: polyethylene terephthalate (PET), polypropylene terephthalate, polybutylene terephthalate (PBT), polyhexylene terephthalate, polyethylene naphthalate (PEN), polybutylene naphthalate (PBN), and polyethylene-1,2-bis(phenoxy)ethane-4,4′-dicarboxylate; and copolymerized polyester-based resins, such as polyethylene isophthalate/terephthalate and polybutylene terephthalate/isophthalate. Among them, polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate, and polybutylene naphthalate, and mixtures thereof having balanced mechanical properties and the like may be preferably used. The compounds preferably have, for example, a ratio “PET:PBT” of from 1:1 to 1:8 (mass ratio) when used in combination.

<Other Components>

Any other additive may be incorporated into the polycarbonate-based resin composition of the present invention to the extent that the effects of the present invention are not impaired. Examples of the other additive may include an antioxidant, a UV absorber, a release agent, a reinforcing material, a filler, an elastomer for an impact resistance improvement, a dye, a pigment, an antistatic agent, and other resins except the polycarbonate.

The polycarbonate-based resin composition of the present invention is obtained by: blending the above-mentioned respective components at the above-mentioned ratios and various optional components to be used as required at appropriate ratios; and kneading the components.

In one aspect of the present invention, the total content of the component (A), the component (B), and the component (C) is preferably from 80 mass % to 100 mass %, more preferably from 95 mass % to 100 mass % with respect to the total amount (100 mass %) of the polycarbonate-based resin composition.

In another aspect of the present invention, the total content of the component (A), the component (B), the component (C), and the above-mentioned other component is preferably from 90 mass % to 100 mass %, more preferably from 95 mass % to 100 mass % with respect to the total amount (100 mass %) of the polycarbonate-based resin composition.

The blending and the kneading may be performed by a method involving premixing with a typically used apparatus, such as a ribbon blender or a drum tumbler, and using, for example, a Henschel mixer, a Banbury mixer, a single-screw extruder, a twin-screw extruder, a multi-screw extruder, or a Ko-kneader. In normal cases, a heating temperature at the time of the kneading is appropriately selected from the range of from 240° C. or more to 320° C. or less. An extruder, in particular a vented extruder is preferably used in the melt-kneading.

[Molded Article]

Various molded bodies may each be produced by an injection molding method, an injection compression molding method, an extrusion molding method, a blow molding method, a press molding method, a vacuum molding method, an expansion molding method, or the like using as a raw material the melt-kneaded polycarbonate-based resin composition of the present invention or a pellet obtained through the melt-kneading. In particular, the pellet obtained through the melt-kneading can be suitably used in the production of injection-molded bodies by injection molding and injection compression molding.

The molded article comprising the polycarbonate-based resin composition of the present invention can be suitably used as, for example: a casing for apart for electrical and electronic equipment, such as a television, a radio, a video camera, a videotape recorder, an audio player, a DVD player, an air conditioner, a cellular phone, a display, a computer, a register, an electronic calculator, a copying machine, a printer, a facsimile, a communication base station, or a battery; or a part for an automobile and a building material.

EXAMPLES

The present invention is more specifically described by way of Examples. However, the present invention is by no means limited by these Examples. In each of Examples, characteristic values and evaluation results were determined in the following manner.

(1) Chain Length and Content of Polydimethylsiloxane

The chain length and content of a polydimethylsiloxane were calculated by NMR measurement from the integrated value ratio of a methyl group of the polydimethylsiloxane. In this description, the polydimethylsiloxane is sometimes abbreviated as PDMS.

<Quantification Method for Chain Length of Polydimethylsiloxane>

¹H-NMR Measurement Conditions

NMR apparatus: ECA500 manufactured by JEOL Resonance Co., Ltd.

Probe: 50TH5AT/FG2

Observed range: −5 ppm to 15 ppm

Observation center: 5 ppm

Pulse repetition time: 9 sec

Pulse width: 45°

NMR sample tube: 5 φ

Sample amount: 30 mg to 40 mg

Solvent: deuterochloroform

Measurement temperature: room temperature

Number of scans: 256 times

Allylphenol-Terminated Polydimethylsiloxane

A: an integrated value of a methyl group in a dimethylsiloxane moiety observed around δ −0.02 to δ 0.5

B: an integrated value of a methylene group in allylphenol observed around δ 2.50 to δ 2.75

Chain length of polydimethylsiloxane=(A/6)/(B/4) Eugenol-terminated Polydimethylsiloxane

A: an integrated value of a methyl group in a dimethylsiloxane moiety observed around δ −0.02 to δ 0.5

B: an integrated value of a methylene group in eugenol observed around δ 2.40 to δ 2.70

Chain length of polydimethylsiloxane=(A/6)/(B/4)

<Quantification Method for Content of Polydimethylsiloxane>

Quantification method for the copolymerization amount of a polydimethylsiloxane in a PTBP-terminated polycarbonate obtained by copolymerizing an allylphenol-terminated polydimethylsiloxane.

NMR apparatus: ECA-500 manufactured by JEOL Resonance Co., Ltd.

Probe: 50TH5AT/FG2

Observed range: −5 ppm to 15 ppm

Observation center: 5 ppm

Pulse repetition time: 9 sec

Pulse width: 45°

Number of scans: 256 times

NMR sample tube: 5 φ

Sample amount: 30 mg to 40 mg

Solvent: deuterochloroform

Measurement temperature: room temperature

A: an integrated value of a methyl group in a BPA moiety observed around δ 1.5 to δ 1.9

B: an integrated value of a methyl group in a dimethylsiloxane moiety observed around δ −0.02 to δ 0.3

C: an integrated value of a butyl group in a p-tert-butylphenyl moiety observed around δ 1.2 to δ 1.4

a=A/6

b=B/6

c=C/9

T=a+b+c

f=a/T×100

g=b/T×100

h=c/T×100

TW=f×254+g×74.1+h×149

PDMS (wt %)=g×74.1/TW×100

(2) Viscosity-Average Molecular Weight

A viscosity-average molecular weight (Mv) was calculated from the following equation (Schnell's equation) by using a limiting viscosity [η] determined through the measurement of the viscosity of a methylene chloride solution at 20° C. with an Ubbelohde-type viscometer.

[η]=1.23×10⁻⁵ ×Mv ^(0.83)

(3) Gel Permeation Chromatography (GPC)

The GPC measurement of a polyorganosiloxane-polycarbonate copolymer was performed under the following conditions.

Test apparatus: PU-2080 manufactured by JASCO Corporation

Solvent: tetrahydrofuran (THF)

Column: TOSOH TSK-GEL MULTIPORE HXL-M×2 and Shodex KR801

Column temperature: 40° C.

Flow rate: 1.0 mL/min

Detector: UV-2075 Plus (254 nm) manufactured by JASCO Corporation

Injection concentration: 10 mg/mL

Injection volume: 0.1 mL

Fraction collector: CHF122SC manufactured by Advantec Co., Ltd.

A standard polystyrene manufactured by Tosoh Corporation was used in the production of a calibration curve.

Under the above-mentioned conditions, the polyorganosiloxane-polycarbonate copolymer was fractionated into 5 fractions for respective retention times to provide fractions. The foregoing operation was repeated 100 times.

The average content and average chain length of the polyorganosiloxane blocks (A-2), the average content of the linking groups of the polycarbonate blocks (A-1) and the polyorganosiloxane blocks (A-2), and the average content of the terminal groups of the polycarbonate blocks (A-1) were determined by the above-mentioned ¹H-NMR measurement for each of the resultant fractions.

In the GPC measurement, in a region corresponding to a molecular weight determined by using a polycarbonate as a conversion reference of from 360 or more to 1,300 or less, a cyclic organosiloxane is detected, and hence the average content and average chain length of the polyorganosiloxane blocks (A-2) apparently seem to be high.

<Production of Polycarbonate Oligomer>

Sodium dithionite was added in an amount of 2,000 ppm with respect to bisphenol A (BPA) (to be dissolved later) to 5.6 mass % aqueous sodium hydroxide, and then BPA was dissolved in the mixture so that the concentration of BPA was 13.5 mass %. Thus, a solution of BPA in aqueous sodium hydroxide was prepared. The solution of BPA in aqueous sodium hydroxide, methylene chloride, and phosgene were continuously passed through a tubular reactor having an inner diameter of 6 mm and a tube length of 30 m at flow rates of 40 L/hr, 15 L/hr, and 4.0 kg/hr, respectively. The tubular reactor had a jacket portion and the temperature of the reaction liquid was kept at 40° C. or less by passing cooling water through the jacket. The reaction liquid that had exited the tubular reactor was continuously introduced into a baffled vessel type reactor provided with a sweptback blade and having an internal volume of 40 L. The solution of BPA in aqueous sodium hydroxide, 25 mass % aqueous sodium hydroxide, water, and a 1 mass % aqueous solution of triethylamine were further added to the reactor at flow rates of 2.8 L/hr, 0.07 L/hr, 17 L/hr, and 0.64 L/hr, respectively, to perform a reaction. An aqueous phase was separated and removed by continuously taking out the reaction liquid overflowing the vessel type reactor and leaving the reaction liquid at rest. Then, a methylene chloride phase was collected.

The polycarbonate oligomer thus obtained had a concentration of 341 g/L and a chloroformate group concentration of 0.71 mol/L.

Production Example 1 <PC-POS Copolymer (A-1a)>

Values for the following (i) to (xiv) are as shown in Table 1.

(i) L of the polycarbonate oligomer solution (PCO) produced as described above, (ii) L of methylene chloride (MC), a solution obtained by dissolving (iv) g of an allylphenol terminal-modified polydimethylsiloxane having an average chain length “n” of (iii) in (v) L of methylene chloride (MC), and (vi) mL of triethylamine (TEA) were loaded into a 50 L vessel-type reactor including a baffle board, a paddle-type stirring blade, and a cooling jacket. (vii) g of 6.4 mass % aqueous sodium hydroxide (NaOHaq) was added to the mixture under stirring, and a reaction between the polycarbonate oligomer and the allylphenol terminal-modified PDMS was performed for 20 minutes.

A solution of p-tert-butylphenol (PTBP) in methylene chloride (obtained by dissolving (viii) g of PTBP in (ix) L of methylene chloride (MC)) and a solution of BPA in aqueous sodium hydroxide (obtained by dissolving (xiii) g of BPA in an aqueous solution obtained by dissolving (x) g of NaOH and (xi) g of sodium dithionite (Na₂S₂O₄) in (xii) L of water) were added to the polymerization liquid, and the mixture was subjected to a polymerization reaction for 40 minutes.

(xiv) L of methylene chloride (MC) was added to the resultant for dilution, and the mixture was stirred for 10 minutes. After that, the mixture was separated into an organic phase containing a PC-POS, and an aqueous phase containing excess amounts of BPA and NaOH, and the organic phase was isolated.

A solution of the PC-POS in methylene chloride thus obtained was sequentially washed with 0.03 mol/L aqueous NaOH and 0.2 mol/L hydrochloric acid in amounts of 15 vol % each with respect to the solution. Next, the solution was repeatedly washed with pure water until an electric conductivity in an aqueous phase after the washing became 0.01 μS/m or less.

The solutions of the polycarbonates in methylene chloride obtained by the washing were concentrated and pulverized, and the resultant flakes were dried under reduced pressure at 120° C. to provide PC-POS copolymers (A1) to (A17). The resultant flake was subjected to the following various kinds of measurement: PDMS content measurement, unreacted PDMS amount measurement, viscosity-average molecular weight measurement, and measurement by GPC. The value of the iM1 of the flake was 3.2, the value of the iM2 thereof was 2.3, the value of the iM3 thereof was 0.7, and the value of the iM1/iA×100 thereof was 287. The other results are shown in Table 1.

TABLE 1 Production Production Example 1 Example 2 PC-POS (A) A-1a A-1b (i) PCO (L) 11 11 (ii) MC (L) 24.5 24.5 (iii) PDMS chain length (n) 61 88 (iv) PDMS loading amount (g) 1,800 1,400 (v) MC (L) 2.0 2.0 (vi) TEA (mL) 6.2 6.2 (vii) NaOHaq (g) 1,405 937 (viii) PTBP (g) 107.6 107.6 (ix) MC (L) 0.5 0.5 (x) NaOH (g) 412 412 (xi) Na₂S₂O₄ (g) 1.5 1.5 (xii) Water (L) 6.0 6.0 (xiii) BPA (g) 766 766 (xiv) MC (L) 0 0 PDMS content (wt %) 30 25 Unreacted PDMS amount (ppm) ≤150 ≤150 Mv 17,700 17,700 wM1 (mass %) 48 41 wM2 (mass %) 30 36 wM3 (mass %) 21 23 wM1/wA × 100 175 167 nM1 76 122 nM2 62 106 nM3 52 84 nM1/nA × 100 125 131

Production Example 2 <PC-POS Copolymer (A-1b)>

Production and measurement were performed in the same manner as in Production Example 1 except that the values (i) to (xiv) were changed as described in Table 1 shown above.

<PC-POS Copolymer (A-2)>

PC-POS copolymer A-2a: “FG1700” [PC-POS copolymer, polyorganosiloxane block chain length: 88, polyorganosiloxane content: 6 mass %, viscosity-average molecular weight Mv: 17,700]

<Aromatic Polycarbonate-Based Resin (B)>

Aromatic polycarbonate-based resin B-1: “FN2500” [viscosity-average molecular weight Mv: 23,500]

Aromatic polycarbonate-based resin B-2: “FN2200” [viscosity-average molecular weight Mv: 21,300]

Aromatic polycarbonate-based resin B-3: “FN1900” [viscosity-average molecular weight Mv: 19,300]

Aromatic polycarbonate-based resin B-4: “FN1700” [viscosity-average molecular weight Mv: 17,700]

<Polyester-Based Resin (C)>

Polyethylene terephthalate: “J055” [manufactured by Mitsui Chemicals, Inc.]

Polyethylene terephthalate: “KS760K-12” [manufactured by Kuraray Co., Ltd.]

Polybutyleneterephthalate: “1401X06” [manufactured by Toray Industries, Inc.]

Polybutylene terephthalate: “DURANEX 2002 EF2001N” [manufactured by Polyplastics Co., Ltd.]

<Other Component>

Antioxidant: “IRGAFOS 168 (product name)” [tris(2,4-di-tert-butylphenyl) phosphite, manufactured by BASF Japan]

Antioxidant: “IRGANOX 1076 (product name)” [octadecyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, manufactured by BASF Japan]

Examples a and b, Examples 1 to 23, and Comparative Examples 1 to 21

The PC-POS copolymers A-1a and A-1b obtained in Production Examples 1 and 2, and the other respective components were mixed at blending ratios shown in Table 2 to Table 6. Each of the mixtures was supplied to a vented twin-screw extruder (manufactured by Toshiba Machine Co., Ltd., TEM-35B), and was melt-kneaded at a screw revolution number of 150 rpm, an ejection amount of 20 kg/hr, and a resin temperature of from 278° C. to 300° C. to provide an evaluation pellet sample. The compositions and evaluation items of PC-based resin compositions are shown in Table 2 to Table 6.

TABLE 2 Example Example Example Example Comparative Comparative Example Example a b 1 2 Example 1 Example 2 3 4 A-1 A-1a (Production parts by mass 8 15 12 Example 1) A-1b (Production parts by mass 9.6 18 14.4 Example 2) A-2 FG1700 parts by mass 75 B B-1 (FN2500) parts by mass 15 15 B-2 (FN2200) parts by mass B-3 (FN1900) parts by mass B-4 (FN1700) parts by mass 92 90.4 60 57 75 48 45.6 C J055 parts by mass 25 25 25 25 25 25 KS760K-12 parts by mass 1401X06 parts by mass Other Irgafos 168 parts by mass 0.05 0.05 0.10 0.10 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 2.4 2.4 6.0 6.0 6.0 0.0 4.8 4.8 content in PC-based resin [(A) + (B)] Viscosity-average molecular — 17,700 17,700 17,700 17,700 17,700 17,700 18,900 18,900 weight (Mv) of PC-based resin [(A) + (B)] MFR (300° C., 1.2 kg) g/10 min — — 13 13 13 21 12 11 Q value (280° C., 160 kg) ×0.01 ml/s 13 13 11 11 11 11 11 10 Izod impact strength (23° C.) kJ/m² 73 74 96 92 91 11 97 99 Izod impact strength (0° C.) kJ/m² — — — — — — — — Izod impact strength (−10° C.) kJ/m² — — 84 83 80 9 83 79 Izod impact strength (−20° C.) kJ/m² — — 74 70 29 9 74 31 Izod impact strength (−30° C.) kJ/m² — — 31 23 19 8 24 19 Izod impact strength (−40° C.) kJ/m² 54 53 — — — — — — Deflection temperature under ° C. 128 128 117 118 117 122 120 120 load Chemical resistance to isobutyl acetate A A A B A A Chemical resistance to toluene A A B B A A Chemical resistance to heptane A A A A A A Comparative Comparative Example Example Comparative Comparative Example 3 Example 4 5 6 Example 5 Example 6 A-1 A-1a (Production parts by mass 7.5 Example 1) A-1b (Production parts by mass 9 Example 2) A-2 FG1700 parts by mass 60 37.5 B B-1 (FN2500) parts by mass 15 37.5 37.5 37.5 B-2 (FN2200) parts by mass 43 B-3 (FN1900) parts by mass 57 32 B-4 (FN1700) parts by mass 18 30 28.5 C J055 parts by mass 25 25 25 25 25 25 KS760K-12 parts by mass 1401X06 parts by mass Other Irgafos 168 parts by mass 0.10 0.10 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 4.8 0.0 3.0 3.0 3.0 0.0 content in PC-based resin [(A) + (B)] Viscosity-average molecular — 18,900 18,900 20,600 20,600 20,600 20,400 weight (Mv) of PC-based resin [(A) + (B)] MFR (300° C., 1.2 kg) g/10 min 11 17 10 11 10 13 Q value (280° C., 160 kg) ×0.01 ml/s 10 10 7.6 7.9 6.8 7.7 Izod impact strength (23° C.) kJ/m² 97 61 97 101 104 82 Izod impact strength (0° C.) kJ/m² — 10 93 96 89 10 Izod impact strength (−10° C.) kJ/m² 76 9 77 57 22 10 Izod impact strength (−20° C.) kJ/m² 13 9 20 18 — 9 Izod impact strength (−30° C.) kJ/m² 16 — 15 14 13 — Izod impact strength (−40° C.) kJ/m² — — — — — — Deflection temperature under ° C. 119 123 122 122 121 124 load Chemical resistance to isobutyl acetate A B A A A B Chemical resistance to toluene A B A A A A Chemical resistance to heptane A A A A A A

TABLE 3 Example Comparative Example Example Comparative 7 Example 7 8 9 Example 8 A-1 A-1a (Production parts by mass 12 7.5 Example 1) A-1b (Production parts by mass 9 Example 2) A-2 FG1700 parts by mass 60 B B-1 (FN2500) parts by mass 15 15 37.5 37.5 37.5 B-2 (FN2200) parts by mass B-3 (FN1900) parts by mass B-4 (FN1700) parts by mass 48 30 28.5 37.5 C J055 parts by mass KS760K-12 parts by mass 25 25 25 25 25 1401X06 parts by mass Other Irgafos 168 parts by mass 0.10 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 4.8 4.8 3.0 3.0 3.0 content in PC-based resin [(A) + (B)] Viscosity-average molecular — 18,900 18,900 20,600 20,600 20,600 weight (Mv) of PC-based resin [(A) + (B)] MFR (300° C., 1.2 kg) g/10 min 14 14 13 13 12 Q value (280° C., 160 kg) ×0.01 ml/s 12 12 11 10 10 Izod impact strength (23° C.) kJ/m² 79 79 92 91 88 Izod impact strength (0° C.) kJ/m² 60 20 74 32 16 Izod impact strength (−10° C.) kJ/m² 25 16 18 16 13 Izod impact strength (−20° C.) kJ/m² — — — — — Izod impact strength (−30° C.) kJ/m² — — — — — Izod impact strength (−40° C.) kJ/m² — — — — — Deflection temperature under ° C. 119 118 121 121 120 load Chemical resistance to isobutyl acetate A A A A A Chemical resistance to toluene A A A A A Chemical resistance to heptane A A A A A Example Example Comparative Comparative 10 11 Example 9 Example 10 A-1 A-1a (Production parts by mass 13.6 Example 1) A-1b (Production parts by mass 16.3 Example 2) A-2 FG1700 parts by mass 68 B B-1 (FN2500) parts by mass 17 17 17 B-2 (FN2200) parts by mass B-3 (FN1900) parts by mass 62 B-4 (FN1700) parts by mass 54.4 51.7 23 C J055 parts by mass 15 15 15 15 KS760K-12 parts by mass 1401X06 parts by mass Other Irgafos 168 parts by mass 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 4.8 4.8 4.8 0.0 content in PC-based resin [(A) + (B)] Viscosity-average molecular — 18,900 18,900 18,900 18,900 weight (Mv) of PC-based resin [(A) + (B)] MFR (300° C., 1.2 kg) g/10 min 12 11 13 18 Q value (280° C., 160 kg) ×0.01 ml/s 9 9 11 9 Izod impact strength (23° C.) kJ/m² 90 89 88 89 Izod impact strength (0° C.) kJ/m² — — — — Izod impact strength (−10° C.) kJ/m² — — — — Izod impact strength (−20° C.) kJ/m² 88 82 75 10 Izod impact strength (−30° C.) kJ/m² 85 77 64 10 Izod impact strength (−40° C.) kJ/m² 69 59 24 9 Deflection temperature under ° C. 123 123 121 126 load Chemical resistance to isobutyl acetate A A A B Chemical resistance to toluene A A B B Chemical resistance to heptane A A A A

TABLE 4 Example Example Comparative Comparative Example Example Comparative 12 13 Example 11 Example 12 14 15 Example 13 A-1 A-1a (Production parts by mass 15.2 13.6 Example 1) A-1b (Production parts by mass 18.2 16.3 Example 2) A-2 FG1700 parts by mass 76 68 B B-1 (FN2500) parts by mass 19 19 19 17 17 17 B-2 (FN2200) parts by mass B-3 (FN1900) parts by mass 70 B-4 (FN1700) parts by mass 60.8 57.8 25 54.4 51.7 C J055 parts by mass 5 5 5 5 KS760K-12 parts by mass 1401X06 parts by mass 15 15 15 Other Irgafos 168 parts by mass 0.10 0.10 0.10 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 4.8 4.8 4.8 0.0 4.8 4.8 4.8 content in PC-based resin [(A) + (B)] Viscosity-average molecular — 18,900 18,900 18,900 18,900 18,900 18,900 18,900 weight (Mv) of PC-based resin [(A) + (B)] MFR (300° C., 1.2 kg) g/10 min 12 12 12 20 42 37 41 Q value (280° C., 160 kg) ×0.01 ml/s 10 10 10 10 29 24 28 Izod impact strength (23° C.) kJ/m² 84 84 84 82 94 103 95 Izod impact strength (0° C.) kJ/m² — — — 54 81 96 85 Izod impact strength (−10° C.) kJ/m² — — — 15 80 87 72 Izod impact strength (−20° C.) kJ/m² — — — — 66 71 20 Izod impact strength (−30° C.) kJ/m² 79 73 73 11 20 20 16 Izod impact strength (−40° C.) kJ/m² 79 70 69 10 — — — Deflection temperature under ° C. 125 125 124 128 102 102 102 load Chemical resistance to Presence or A A A B A A A isobutyl acetate absence of breakage Whitening B B B B B B B Chemical resistance to Presence or A A A A A A A heptane absence of crack Comparative Example Example Comparative Comparative Example 14 16 17 Example 15 Example 16 A-1 A-1a (Production parts by mass 15.2 Example 1) A-1b (Production parts by mass 18.2 Example 2) A-2 FG1700 parts by mass 76 B B-1 (FN2500) parts by mass 19 19 19 B-2 (FN2200) parts by mass B-3 (FN1900) parts by mass 62 70 B-4 (FN1700) parts by mass 23 60.8 57.8 25 C J055 parts by mass KS760K-12 parts by mass 1401X06 parts by mass 15 5 5 5 5 Other Irgafos 168 parts by mass 0.10 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 0.0 4.8 4.8 4.8 0.0 content in PC-based resin [(A) + (B)] Viscosity-average molecular — 18,900 18,900 18,900 18,900 18,900 weight (Mv) of PC-based resin [(A) + (B)] MFR (300° C., 1.2 kg) g/10 min 43 18 17 22 27 Q value (280° C., 160 kg) ×0.01 ml/s 21 13 13 15 14 Izod impact strength (23° C.) kJ/m² 7 86 87 88 11 Izod impact strength (0° C.) kJ/m² 8 — — — — Izod impact strength (−10° C.) kJ/m² 7 — — — — Izod impact strength (−20° C.) kJ/m² 8 — — — — Izod impact strength (−30° C.) kJ/m² 7 75 72 69 9 Izod impact strength (−40° C.) kJ/m² — 68 67 63 9 Deflection temperature under ° C. 105 118 118 117 121 load Chemical resistance to Presence or B B B B C isobutyl acetate absence of breakage Whitening B B B B B Chemical resistance to Presence or B A A B B heptane absence of crack

TABLE 5 Example Example Comparative Comparative Comparative 18 19 Example 17 Example 18 Example 19 A-1 A-1a (Production parts by mass 7.5 Example 1) A-1b (Production parts by mass 9 Example 2) A-2 FG1700 parts by mass 37.5 80 B B-1 (FN2500) parts by mass 37.5 37.5 37.5 20 B-2 (FN2200) parts by mass 43 B-3 (FN1900) parts by mass 32 B-4 (FN1700) parts by mass 30 28.5 C J055 parts by mass KS760K-12 parts by mass 1401X06 parts by mass 25 25 25 25 Other Irgafos 168 parts by mass 0.10 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 3.0 3.0 3.0 0.0 4.8 content in PC-based resin [(A) + (B)] Viscosity-average molecular — 20,600 20,600 20,600 20,400 18,900 weight (Mv) of PC-based resin [(A) + (B)] MFR (300° C., 1.2 kg) g/10 min 65 74 65 70 12 Q value (280° C., 160 kg) ×0.01 ml/s 25 25 36 33 10 Izod impact strength (23° C.) kJ/m² 80 81 80 6 79 Izod impact strength (0° C.) kJ/m² — — — 7 76 Izod impact strength (−10° C.) kJ/m² 12 13 13 7 73 Izod impact strength (−20° C.) kJ/m² 11 12 12 7 72 Izod impact strength (−30° C.) kJ/m² — — — — 70 Izod impact strength (−40° C.) kJ/m² — — — — 68 Deflection temperature under ° C. 90 91 91 91 127 load Chemical resistance to isobutyl acetate A A A B C Chemical resistance to toluene A A A A B Chemical resistance to heptane A A A B B

TABLE 6 Comparative Example Example Comparative Example Example Example 20 20 21 Example 21 22 23 A-1 A-1a (Production parts by mass 12 7.5 Example 1) A-1b (Production parts by mass 14.4 9 Example 2) A-2 FG1700 parts by mass 60 37.5 B B-1 (FN2500) parts by mass 15 15 15 37.5 37.5 37.5 B-2 (FN2200) parts by mass B-3 (FN1900) parts by mass B-4 (FN1700) parts by mass 45.6 48 28.5 30 C J055 parts by mass KS760K-12 parts by mass 1401X06 parts by mass 2002 EF2001N parts by mass 25 25 25 25 25 25 Other Irgafos 168 parts by mass 0.10 0.10 0.10 0.10 0.10 0.10 Irganox 1076 parts by mass 0.10 0.10 0.10 0.10 0.10 0.10 Polyorganosiloxane block mass % 4.8 4.8 4.8 3.0 3.0 3.0 content in PC-based resin [(A) + (B)] Viscosity-average molecular — 18,900 18,900 18,900 20,600 20,600 20,600 weight (Mv) of PC-based resin [(A) + (B)] MFR (300° C., 1.2 kg) g/10 min 32 29 30 29 27 28 Q value (280° C., 160 kg) x0.01 ml/s 21 19 21 16 15 15 Izod impact strength (23° C.) kJ/m² 106 123 113 93 118 104 Izod impact strength (0° C.) kJ/m² 98 111 107 14 99 97 Izod impact strength (−10° C.) kJ/m² 55 105 104 13 19 88 Izod impact strength (−20° C.) kJ/m² 16 97 97 12 16 17 Izod impact strength (−30° C.) kJ/m² 15 83 88 11 15 15 Izod impact strength (−40° C.) kJ/m² — — — — — — Deflection temperature under ° C. 88 88 86 90 89 89 load Chemical resistance to isobutyl acetate A A A A A A Chemical resistance to toluene A A A A A A Chemical resistance to heptane A A A A A A

[Evaluation Test] <Fluidity Evaluation>(MFR)

The amount (g/10 min) of a molten resin flowing out of a die having a diameter of 2.095±0.005 mm and a length of 8.000±0.025 mm was measured by using the above-mentioned pellet in conformity with JIS K 7210-1:2014 at 300° C. under a load of 1.2 kg.

<Q Value (Flow Value) [Unit; 10⁻² mL/Sec]>

The amount (mL/sec) of a molten resin flowing out of a nozzle having a diameter of 1.00 mm and a length of 10.00 mm was measured by using the above-mentioned pellet and a Koka flow tester in conformity with JIS K 7210-1:2014: Appendix JA at 280° C. under a pressure of 160 kgf. A Q value represents an outflow amount per unit time, and a higher numerical value therefor means that the fluidity of the resin is better.

<Impact Resistance>

The pellet obtained in the foregoing was dried at 120° C. for 8 hours, and was then subjected to injection molding with an injection molding machine (manufactured by Nissei Plastic Industrial Co., Ltd., NEX110, screw diameter: 36 mmφ) at a cylinder temperature of 280° C. and a die temperature of 80° C. to produce an Izod test piece (length: 63.5 mm, width: 12.7 mm, thickness: 3.2 mm). Notched Izod impact strengths at −40° C., −30° C., −20° C., −10° C., 0° C., and 23° C. were measured by using a test piece obtained by making a notch (r=0.25 mm±0.05 mm) in the test piece through post-processing in conformity with ASTM Standard D-256.

<Deflection Temperature Under Load (Unit; ° C.)>

The pellet obtained in the foregoing was dried at 120° C. for 8 hours, and was then subjected to injection molding with an injection molding machine (manufactured by Nissei Plastic Industrial Co., Ltd., NEX110, screw diameter: 36 mmφ) at a cylinder temperature of 280° C. and a die temperature of 80° C. to provide a test piece (length: 127 mm, width: 12.7 mm, thickness: 3.2 mm). A load of 1.8 MPa was applied to the test piece in conformity with ASTM Standard D-648 at a rate of temperature increase of 120° C./h and a fulcrum-to-fulcrum distance of 100 mm, and the temperature at which the deflection of the test piece measured in an edgewise manner reached 0.26 mm was recorded.

<Chemical Resistance to Isobutyl Acetate>

The pellet obtained in the foregoing was subjected to injection molding at a molding temperature of 280° C. and a die temperature of 80° C. to provide a test piece measuring 127 mm long by 12.7 mm wide by 3.2 mm thick. A strain of 1.0% was applied to the test piece by a three-point bending test method at a span distance of 80 mm, and then isobutyl acetate was applied thereto with a swab. The test piece was left to stand at 23° C. for 2 minutes, and then a change in appearance thereof was observed, followed by an evaluation in accordance with the following criteria.

A case in which the sample was free of any appearance change or a fine crack occurred on its surface was indicated by Symbol “A”.

A case in which a crack arrived from the surface of the sample to the opposite surface thereof in the thickness direction thereof was indicated by Symbol “B”.

A case in which the sample broke and hence no stress was applied thereto with a jig was indicated by Symbol “C”.

<Chemical Resistance to Toluene>

The pellet obtained in the foregoing was subjected to injection molding at a molding temperature of 280° C. and a die temperature of 80° C. to provide a test piece measuring 127 mm long by 12.7 mm wide by 3.2 mm thick. A strain of 1.0% was applied to the test piece by a three-point bending test method at a span distance of 80 mm, and then two drops of toluene was applied thereto with a pipette. The test piece was left to stand at 23° C. for 15 minutes, and then a change in appearance thereof was observed, followed by an evaluation in accordance with the following criteria.

A case in which the test piece did not whiten was indicated by Symbol “A”.

A case in which the test piece whitened was indicated by Symbol “B”.

<Chemical Resistance to Heptane>

The pellet obtained in the foregoing was subjected to injection molding at a molding temperature of 280° C. and a die temperature of 80° C. to provide a test piece measuring 127 mm long by 12.7 mm wide by 3.2 mm thick. A strain of 1.0% was applied to the test piece by a three-point bending test method at a span distance of 80 mm, and then a cloth was placed on the strained portion. Heptane was continuously dropped on the cloth at 23° C. for 30 minutes, and then a change in appearance of the test piece was observed, followed by an evaluation in accordance with the following criteria.

A case in which no crack occurred on the surface of the test piece was indicated by Symbol “A”.

A case in which a crack occurred on the surface of the test piece was indicated by Symbol “B”.

INDUSTRIAL APPLICABILITY

The polycarbonate resin obtained in the present invention can be suitably used as a casing and the like for a part for electrical and electronic equipment, and a part and the like for an automobile and a building material because the resin is excellent in impact resistance. 

1-13. (canceled)
 14. The polycarbonate-polyorganosiloxane copolymer according to claim 20, wherein the aromatic polycarbonate-based resin (B) contains a polycarbonate block including, in a main chain thereof, a repeating unit represented by the following general formula (III):

wherein R³⁰ and R³¹ each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X′ represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, —S—, —SO—, —SO₂—, —O—, or —CO—, and “d” and “e” each independently represent an integer of from 0 to
 4. 15-19. (canceled)
 20. A polycarbonate-based resin composition, comprising: a polycarbonate-polyorganosiloxane copolymer (A) comprising polycarbonate blocks (A-1) each formed of a repeating unit represented by the following general formula (I); and polyorganosiloxane blocks (A-2) each containing a repeating unit represented by the following general formula (II), wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F1a): 15≤wM1  (F1a) wherein wM1 represents an average content (mass %) of the polyorganosiloxane blocks (A-2) in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using a polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among polycarbonate-polyorganosiloxane copolymers obtained through separation of the polycarbonate-polyorganosiloxane copolymer by gel permeation chromatography; an aromatic polycarbonate-based resin (B) except the polycarbonate-polyorganosiloxane copolymer (A); and a polyester-based resin (C), wherein the polyester-based resin (C) is blended with respect to 100 parts by mass of a total of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B), and wherein a ratio of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) in 100 mass % of a total amount of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B), and the polyester-based resin (C) is from 50 mass % or more to 99 mass % or less:

wherein R¹ and R² each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, a fluorenediyl group, an arylalkylene group having 7 to 15 carbon atoms, an arylalkylidene group having 7 to 15 carbon atoms, —S—, —SO—, —SO₂—, —O—, or —CO—, R³ and R⁴ each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and “a” and “b” each independently represent an integer of from 0 to
 4. 21. The polycarbonate-based resin composition according to claim 20, wherein a mass ratio “(A)/(B)” of the polycarbonate-polyorganosiloxane copolymer (A) to the aromatic polycarbonate-based resin (B) is from 0.1/99.9 to 99.9/0.1.
 22. The polycarbonate-based resin composition according to claim 20, wherein a content of the polyorganosiloxane blocks (A-2) with respect to a total of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) is from 0.1 mass % or more to 10 mass % or less.
 23. The polycarbonate-based resin composition according to claim 20, wherein a polycarbonate-based resin formed of the polycarbonate-polyorganosiloxane copolymer (A) and the aromatic polycarbonate-based resin (B) has a viscosity-average molecular weight (Mv) of from 9,000 or more to 50,000 or less.
 24. The polycarbonate-based resin composition according to claim 20, wherein the polyester-based resin (C) comprises at least one selected from a polyethylene terephthalate and a polybutylene terephthalate.
 25. A molded article, which is obtained by molding the polycarbonate-based resin composition of claim
 20. 26. The molded article according to claim 25, wherein the molded article comprises a casing for electrical and electronic equipment.
 27. The molded article according to claim 25, wherein the molded article comprises a part for an automobile and a building material. 